Effect of fatigue precracking on crack engagement during sonic IR testing

William Riddell, John C. Chen, Chang Hwa Wong

Research output: Contribution to journalArticlepeer-review

Abstract

A series of sonic IR tests were performed on modified eccentrically-loaded single edge tension [ESE(T)] specimens in which crack lengths were nominally identical, but the precracking load history used to develop the sharp cracks used in the tests was varied from specimen to specimen. A measure for crack engagement length, defined as the length of crack that develops heat during sonic IR inspection was established for these tests. The result suggest that, in a certain regime, crack engagement length correlates with fatigue opening load, which is the stress intensity factor at which the crack front is fully open during the fatigue precracking. The implication of this is that laboratory test results for sonic IR should be performed with test specimens that have undergone careful precracking procedures, and that these procedures should be reported with test results.

Original languageEnglish (US)
Pages (from-to)18-34
Number of pages17
JournalResearch in Nondestructive Evaluation
Volume24
Issue number1
DOIs
StatePublished - Jan 1 2013

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering
  • Materials Science(all)

Fingerprint

Dive into the research topics of 'Effect of fatigue precracking on crack engagement during sonic IR testing'. Together they form a unique fingerprint.

Cite this