N2 - Poly(ethylene glycol) (PEG) is widely used to modulate the hydration states of biomaterials and is often applied to produce nonfouling surfaces. Here, we present X-ray scattering data, which show that it is the surface segregation of PEG, not just its presence in the bulk, that makes this happen by influencing the hydrophilicity of PEG-containing substrates. We demonstrate a temperature-dependent trigger that transforms a PEG-containing substrate from a protein-adsorbing to a protein-repelling state. On films of poly(desaminotyrosyl-tyrosine-co-PEG carbonate) with high (20 wt %) PEG content, in which very little protein adsorption is expected, quartz crystal microbalance data showed significant adsorption of fibrinogen and bovine serum albumin at 8 °C. The surface became protein-repellent at 37.5 °C. When the same polymer was iodinated, the polymer was protein-adsorbent, even when 37 wt % PEG was incorporated into the polymer backbone. This demonstrates that high PEG content by itself is not sufficient to repel proteins. By inhibiting phase separation either with iodine or by lowering the temperature, we show that PEG must phase-separate and bloom to the surface to create an antifouling surface. These results suggest an opportunity to design materials with high PEG content that can be switched from a protein-attractant to a protein-repellent state by inducing phase separation through brief exposure to temperatures above their glass transition temperature.
AB - Poly(ethylene glycol) (PEG) is widely used to modulate the hydration states of biomaterials and is often applied to produce nonfouling surfaces. Here, we present X-ray scattering data, which show that it is the surface segregation of PEG, not just its presence in the bulk, that makes this happen by influencing the hydrophilicity of PEG-containing substrates. We demonstrate a temperature-dependent trigger that transforms a PEG-containing substrate from a protein-adsorbing to a protein-repelling state. On films of poly(desaminotyrosyl-tyrosine-co-PEG carbonate) with high (20 wt %) PEG content, in which very little protein adsorption is expected, quartz crystal microbalance data showed significant adsorption of fibrinogen and bovine serum albumin at 8 °C. The surface became protein-repellent at 37.5 °C. When the same polymer was iodinated, the polymer was protein-adsorbent, even when 37 wt % PEG was incorporated into the polymer backbone. This demonstrates that high PEG content by itself is not sufficient to repel proteins. By inhibiting phase separation either with iodine or by lowering the temperature, we show that PEG must phase-separate and bloom to the surface to create an antifouling surface. These results suggest an opportunity to design materials with high PEG content that can be switched from a protein-attractant to a protein-repellent state by inducing phase separation through brief exposure to temperatures above their glass transition temperature.
UR - http://www.scopus.com/inward/record.url?scp=85070720600&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85070720600&partnerID=8YFLogxK
U2 - 10.1021/acs.langmuir.9b00702
DO - 10.1021/acs.langmuir.9b00702
M3 - Article
C2 - 31257890
SN - 0743-7463
VL - 35
SP - 9769
EP - 9776
JO - Langmuir
JF - Langmuir
IS - 30
ER -